| Type |
Photo |
Description |
| Slot Die type |
 |
- Coating is possible in vertical, horizontal, and side directions
- Coating Thickness: 3-50 μm (wet)
- Viscosity Range: 1,000~10,000 cP (mPa·s)
- Coating Speed: ~200m/min
|
| COMMA type |
 |
- Coating Thickness: 20-150 μm (wet)
- Viscosity Range: 1,000~10,000 cP (mPa·s)
- Coating Speed: ~200m/min
|
| Closed chamber gravure type |
 |
- Chambered double blade ink supply system ensures complete ink removal without being affected by speed
- High mesh count rollers and high viscosity inks can be used
- Coating Thickness: 1-20 μm (wet)
- Viscosity Range: 1~100 cP (mPa·s)
- Coating Speed: ~100m/min
|
| Micro gravure type |
 |
- The coating area can be adjusted based on the engraving method
- Fully coated or edge areas reserved
- Coating Thickness: 1-20 μm (wet)
- Viscosity Range: 1~100 cP (mPa·s)
- Coating Speed: ~100m/min
|
| Roll to Roll type-1 |
 |
- The coating amount is adjusted by modifying the roller gap and speed
- Viscosity Range: 10~500 cP (mPa·s)
|
| Roll to Roll type-2 |
 |
- Easily controlling tension ensures stable coating precision
- Economic cost
- Coating Thickness: 3-50 μm (wet)
- Viscosity Range: 1,000~10,000 cP (mPa·s)
- Coating Speed: ~200m/min
|
| Blade type |
 |
- Precise coating thickness
- Viscosity Range: mediμm→high
|
| D-bar type |
 |
- High Speed, Ultra Thin Coating
- Anti-Bubble
- Viscosity Range: 1~3,000 cP (mPa·s)
|
| Two-sided type |
 |
- Coating on both sides simultaneously is possible
- Different patterns on both sides are possible
- Viscosity Range: mediμm
|
| Gravure type |
 |
- Excellent coating amount, stable coating precision
- Easy to operate
- Coating Thickness: 1-40 μm (wet)
- Viscosity Range: 1~1,500 cP (mPa·s)
- Coating Speed: ~200m/min
|
| Tension control roll type |
 |
- Embossed structures made with coating area
- Viscosity Range: 1~3,000 cP (mPa·s)
|
| Tension control die type |
 |
- Capable of high-speed, thin-film coating
- Viscosity Range: Low
|
| Spray type |
 |
- Uniform and ultra-thin coating
- Viscosity Range: Low
|
| The hot melt rubber type |
 |
- Environmentally friendly, 100% solids content, solvent-free, with no drying process required, and reduced coating process time
- Coating Thickness: 20-250 μm (wet)
- Viscosity Range: 1,000~10,000 cP (mPa·s)
|
| Dip type-1 |
 |
- Suitable for organic porous substrates
- Suitable for various coatings
- Viscosity Range: 10~2,000 cP (mPa·s)
|
| Dip type-2 |
 |
- Suitable for flexible packaging materials such as carbon fiber, aluminum-plastic film, and copper foil.
- Coating Thickness: 20-250 μm (wet)
- Viscosity Range: 1~100 cP (mPa·s)
|